Formation of boride barrier layers using chemisorption techniques

ABSTRACT

In one embodiment, a method for depositing a boride-containing barrier layer on a substrate is provided which includes exposing the substrate sequentially to a boron-containing compound and a metal precursor to form a first boride-containing layer during a first sequential chemisorption process and exposing the substrate to the boron-containing compound, the metal precursor, and a second precursor to form a second boride-containing layer on the first boride-containing layer during a second sequential chemisorption process. In one example, the metal precursor contains tungsten hexafluoride and the boron-containing compound contains diborane. In another embodiment, a contact layer is deposited over the second boride-containing layer. The contact layer may contain tungsten and be deposited by a chemical vapor deposition process. Alternatively, the contact layer may contain copper and be deposited by a physical vapor deposition process. In other examples, boride-containing layers may be formed at a temperature of less than about 500° C.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. Ser. No. 10/993,925 (APPM/004417.C2), filed Nov. 19, 2004, and issued as U.S. Pat. No. 7,208,413, which is a continuation of U.S. Ser. No. 10/387,990 (APPM/004417.C1), filed Mar. 13, 2003, issued as U.S. Pat. No. 6,831,004, which is a continuation of U.S. Ser. No. 09/604,943 (APPM/004417), filed Jun. 27, 2000, issued as U.S. Pat. No. 6,620,723, which are all herein incorporated in their entirety by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to the formation of boride barrier layers and, more particularly to boride barrier layers formed using chemisorption techniques.

2. Description of the Related Art

In the manufacture of integrated circuits, barrier layers are often used to inhibit the diffusion of metals and other impurities into regions underlying such barrier layers. These underlying regions may include transistor gates, capacitor dielectric, semiconductor substrates, metal lines, as well as many other structures that appear in integrated circuits.

For the current sub-micron (0.5 μm) generation of semiconductor devices, any microscopic reaction at an interface between interconnection layers can cause degradation of the resulting integrated circuits (e.g., increase the resistivity of the interconnection layers). Consequently, barrier layers have become a critical component for improving the reliability of interconnect metallization schemes.

Compounds of refractory metals such as, for example, nitrides, borides, and carbides have been suggested as diffusion barriers because of their chemical inertness and low resistivity (e.g., resistivity typically less than about 200 μΩ-cm). In particular, borides such as, for example, titanium diboride (TiB₂) have been suggested for use as a barrier material since layers formed thereof generally have low resistivity (e.g., resistivity less than about 150 μΩ-cm).

Boride barrier layers are typically formed using chemical vapor deposition (CVD) techniques. For example, titanium tetrachloride (TiCl₄) may be reacted with diborane (B₂H₆) to form titanium diboride using CVD. However, when Cl-based chemistries are used to form boride barrier layers, reliability problems can occur. In particular, boride layers formed using CVD chlorine-based chemistries typically have a high chlorine content (e.g., chlorine content greater than about 3%). A high chlorine content is undesirable because the chlorine may migrate from the boride barrier layer into adjacent interconnection layers, which can increase the contact resistance of such interconnection layers and potentially change the characteristics of integrated circuits made therefrom.

Therefore, a need exists in the art for reliable boride barrier layers for integrated circuit fabrication. Particularly desirable would be reliable boride barrier layers useful for interconnect structures.

SUMMARY OF THE INVENTION

Boride barrier layers for integrated circuit fabrication are provided. In one embodiment, the boride barrier layer comprises one refractory metal. The boride barrier layer may be formed by sequentially chemisorbing alternating monolayers of a boron compound and a refractory metal compound onto a substrate.

In an alternate embodiment, a composite boride barrier layer is formed. The composite boride barrier layer comprises two or more refractory metals. The composite boride barrier layer may be formed by sequentially chemisorbing monolayers of a boron compound and two or more refractory metal compounds onto a substrate.

The boride barrier layer is compatible with integrated circuit fabrication processes. In one integrated circuit fabrication process, the boride barrier layer comprises one refractory metal. The boride barrier layer is formed by sequentially chemisorbing alternating monolayers of a boron compound and one refractory metal compound on a substrate. Thereafter, one or more metal layers are deposited on the boride barrier layer to form an interconnect structure.

In another integrated circuit fabrication process, the boride barrier layer has a composite structure. The composite boride barrier layer comprises two or more refractory metals. The composite boride barrier layer is formed by sequentially chemisorbing monolayers of a boron compound and two or more refractory metal compounds on a substrate. Thereafter, one or more metal layers are deposited on the composite boride barrier layer to form an interconnect structure.

BRIEF DESCRIPTION OF THE DRAWINGS

The teachings of the present invention can be readily understood by considering the following detailed description in conjunction with the accompanying drawings, in which:

FIG. 1 depicts a schematic illustration of an apparatus that can be used for the practice of embodiments described herein;

FIGS. 2A-2C depict cross-sectional views of a substrate structure at different stages of integrated circuit fabrication incorporating a boride barrier layer;

FIGS. 3A-3C depict cross-sectional views of a substrate undergoing a first sequential chemisorption process of a boron compound and one refractory metal compound to form a boride barrier layer;

FIGS. 4A-4D depict cross-sectional views of a substrate undergoing a second sequential chemisorption process of a boron compound and two refractory metal compounds to form a composite boride barrier layer;

FIGS. 5A-5D depict cross-sectional views of a substrate undergoing a third sequential chemisorption of a boron compound and two refractory metal compounds to form a composite boride barrier layer; and

FIGS. 6A-6C depict cross-sectional views of a substrate structure at different stages of integrated circuit fabrication incorporating more than one boride barrier layer.

DETAILED DESCRIPTION

FIG. 1 depicts a schematic illustration of a wafer processing system 10 that can be used to form boride barrier layers in accordance with embodiments described herein. The system 10 comprises a process chamber 100, a gas panel 130, a control unit 110, along with other hardware components such as power supplies 106 and vacuum pumps 102. The salient features of process chamber 100 are briefly described below.

Chamber 100

The process chamber 100 generally houses a support pedestal 150, which is used to support a substrate such as a semiconductor wafer 190 within the process chamber 100. Depending on the specific process, the semiconductor wafer 190 can be heated to some desired temperature prior to layer formation.

In chamber 100, the wafer support pedestal 150 is heated by an embedded heater 170. For example, the pedestal 150 may be resistively heated by applying an electric current from an AC power supply 106 to the heater element 170. The wafer 190 is, in turn, heated by the pedestal 150, and can be maintained within a desired process temperature range of, for example, about 20° C. to about 500° C.

A temperature sensor 172, such as a thermocouple, is also embedded in the wafer support pedestal 150 to monitor the temperature of the pedestal 150 in a conventional manner. For example, the measured temperature may be used in a feedback loop to control the electric current applied to the heater element 170 by the power supply 106, such that the wafer temperature can be maintained or controlled at a desired temperature that is suitable for the particular process application. The pedestal 150 is optionally heated using radiant heat (not shown).

A vacuum pump 102 is used to evacuate process gases from the process chamber 100 and to help maintain the desired pressure inside the chamber 100. An orifice 120 is used to introduce process gases into the process chamber 100. The dimensions of the orifice 120 are variable and typically depend on the size of the process chamber 100.

The orifice 120 is coupled to a gas panel 130 via a valve 125. The gas panel 130 provides process gases from two or more gas sources 135, 136 to the process chamber 100 through orifice 120 and valve 125. The gas panel 130 also provides a purge gas from a purge gas source 138 to the process chamber 100 through orifice 120 and valve 125.

A control unit 110, such as a computer, controls the flow of various process gases through the gas panel 130 as well as valve 125 during the different steps of a wafer process sequence. Illustratively, the control unit 110 comprises a central processing unit (CPU) 112, support circuitry 114, and memories containing associated control software 116. In addition to the control of process gases through the gas panel 130, the control unit 110 is also responsible for automated control of the numerous steps required for wafer processing—such as wafer transport, temperature control, chamber evacuation, among other steps.

The control unit 110 may be one of any form of general purpose computer processor that can be used in an industrial setting for controlling various chambers and sub-processors. The computer processor may use any suitable memory, such as random access memory, read only memory, floppy disk drive, hard disk, or any other form of digital storage, local or remote. Various support circuits may be coupled to the computer processor for supporting the processor in a conventional manner. Software routines as required may be stored in the memory or executed by a second processor that is remotely located. Bi-directional communications between the control unit 110 and the various components of the wafer processing system 10 are handled through numerous signal cables collectively referred to as signal buses 118, some of which are illustrated in FIG. 1.

Boride Barrier Layer Formation

FIGS. 2A-2C illustrate one preferred embodiment of boride layer formation for integrated circuit fabrication of an interconnect structure. In general, the substrate 200 refers to any workpiece upon which film processing is performed, and a substrate structure 250 is used to generally denote the substrate 200 as well as other material layers formed on the substrate 200. Depending on the specific stage of processing, the substrate 200 may be a silicon semiconductor wafer, or other material layer, which has been formed on the wafer. FIG. 2A, for example, shows a cross-sectional view of a substrate structure 250, having a material layer 202 thereon. In this particular illustration, the material layer 202 may be an oxide (e.g., silicon dioxide). The material layer 202 has been conventionally formed and patterned to provide a contact hole 202H extending to the top surface 200T of the substrate 200.

FIG. 2B shows a boride layer 204 conformably formed on the substrate structure 250. The boride layer 204 is formed by chemisorbing monolayers of a boron-containing compound and a refractory metal compound on the substrate structure 250.

The monolayers are chemisorbed by sequentially providing a boron-containing compound and one or more refractory metal compounds to a process chamber. In a first sequential chemisorption process, the monolayers of the boron-containing compound and one refractory metal compound are alternately chemisorbed on a substrate 300 as shown in FIGS. 3A-3C.

FIG. 3A depicts a cross-sectional view of a substrate 300, which may be in a stage of integrated circuit fabrication. A monolayer of a boron-containing compound 305 is chemisorbed on the substrate 300 by introducing a pulse of a boron-containing gas into a process chamber similar to that shown in FIG. 1. The boron-containing compound typically combines boron atoms 310 with one or more reactive species b 315. During boride layer formation, the reactive species b 315 form byproducts that are transported from the surface of substrate 300 by the vacuum system.

The chemisorbed monolayer of the boron-containing compound 305 is self-limiting in that only one monolayer may be chemisorbed onto the surface of substrate 300 during a given pulse. Only one monolayer of the boron-containing compound is chemisorbed on the substrate because the substrate has a limited surface area. This limited surface area provides a finite number of sites for chemisorbing the boron-containing compound. Once the finite number of sites is occupied by the boron-containing compound, further chemisorption of the boron-containing compound will be blocked.

The boron-containing compound may be for example a borane compound having the general formula B_(x)H_(y), where x has a range between 1 and 10, and y has a range between 3 and 30. For example, borane (BH₃), diborane (B₂H₆), triborane, tetraborane, pentaborane, hexaborane, heptaborane, octaborane, nonaborane, and decaborane, may be used as the boron-containing compound.

After the monolayer of the boron compound is chemisorbed onto the substrate 300, excess boron-containing compound is removed from the process chamber by introducing a pulse of a purge gas thereto. Purge gases such as, for example, helium, argon, nitrogen (N₂), ammonia (NH₃), and hydrogen (H₂), among others may be used.

After the process chamber has been purged, a pulse of one refractory metal compound is introduced into the process chamber. Referring to FIG. 3B, a layer of the refractory metal compound 307 is chemisorbed on the boron monolayer 305. The refractory metal compound typically combines refractory metal atoms 320 with one or more reactive species a 325.

The chemisorbed monolayer of the refractory metal compound 307 reacts with the boron-containing monolayer 305 to form a boride layer 309. The reactive species a 325 and b 315 form byproducts ab 330 that are transported from the substrate 300 surface by the vacuum system. The reaction of the refractory metal compound 307 with the boron monolayer 305 is self-limited, since only one monolayer of the boron compound was chemisorbed onto the substrate 300 surface.

The refractory metal compound may include refractory metals such as for example titanium, tungsten, tantalum, zirconium, hafnium, molybdenum, niobium, vanadium, and chromium, among others combined with reactive species such as, for example chlorine and fluorine. For example, titanium tetrachloride (TiCl₄), tungsten hexafluoride (WF₆), tantalum pentachloride (TaCl₅), zirconium tetrachloride (ZrCl₄), hafnium tetrachloride (HfCl₄), molybdenum pentachloride (MOCl₅), niobium pentachloride (NbCl₅), vanadium pentachloride (VCl₅), chromium tetrachloride (CrCl₄) may be used as the refractory metal compound.

After the monolayer of the refractory metal compound is chemisorbed onto the substrate 300, any excess refractory metal compound is removed from the process chamber by introducing another pulse of the purge gas therein. Thereafter, as shown in FIG. 3C, the boride layer deposition sequence of alternating monolayers of the boron-containing compound and the refractory metal compound are repeated until a desired boride layer thickness is achieved. The boride layer may, for example, have a thickness in a range of about 200 Å to about 5,000 Å, and more preferably, about 2,500 Å.

In FIGS. 3A-3C, boride layer formation is depicted as starting with the chemisorption of a boron-containing monolayer on the substrate followed by a monolayer of a refractory metal compound. Alternatively, the boride layer formation may start with the chemisorption of a monolayer of a refractory metal compound on the substrate followed by a monolayer of the boron-containing compound.

The pulse time for each pulse of the boron-containing compound, the one or more refractory metal compounds, and the purge gas is variable and depends on the volume capacity of the deposition chamber as well as the vacuum system coupled thereto. Similarly, the time between each pulse is also variable and depends on the volume capacity of the process chamber as well as the vacuum system coupled thereto.

In general, the alternating monolayers may be chemisorbed at a substrate temperature less than about 500° C., and a chamber pressure less than about 100 Torr. A pulse time of less than about 1 second for the boron-containing compound, and a pulse time of less than about 1 second for the refractory metal compounds are typically sufficient to chemisorb the alternating monolayers that comprise the boride layer on the substrate. A pulse time of less than about 1 second for the purge gas is typically sufficient to remove the reaction byproducts as well as any residual materials remaining in the process chamber.

In a second chemisorption process, the boron-containing monolayers and two or more refractory metal compounds are alternately chemisorbed on the substrate to form a composite boride layer. FIG. 4A depicts a cross-sectional view of a substrate 400, which may be in a stage of integrated circuit fabrication. A self-limiting monolayer of a boron-containing compound 405 is chemisorbed on the substrate 400 by introducing a pulse of a boron-containing compound into a process chamber similar to that shown in FIG. 1 according to the process conditions described above with reference to FIGS. 2A-2C. The boron-containing compound combines boron atoms 410 with one or more reactive species b 415.

After the monolayer of the boron compound 405 is chemisorbed onto the substrate 400, excess boron-containing compound is removed from the process chamber by introducing a pulse of a purge gas thereto.

Referring to FIG. 4B, after the process chamber has been purged, a pulse of a first refractory metal compound M₁a₁ is introduced into the process chamber. A layer of the first refractory metal compound 407 is chemisorbed on the boron monolayer 405. The first refractory metal compound typically combines first refractory metal atoms M₁ 420 with one or more reactive species a₁ 425.

The chemisorbed monolayer of the first refractory metal compound 407 reacts with the boron-containing monolayer 405 to form a boride monolayer 409. The reactive species a₁, 425 and b 415 form byproducts a₁b 430 that are transported from the substrate 400 surface by the vacuum system.

After the monolayer of the first refractory metal compound 407 is chemisorbed onto the substrate 400, the excess first refractory metal compound M₁a₁ is removed from the process chamber by introducing another pulse of the purge gas therein.

Another pulse of the boron-containing compound is than introduced into the process chamber. A monolayer of the boron-containing compound 405 is chemisorbed on the first refractory metal monolayer 407, as shown in FIG. 4C. The chemisorbed monolayer of the boron-containing compound 405 reacts with the first refractory metal monolayer 407 to form a boride layer 409. The reactive species a₁ 425 and b 415 form byproducts a₁b 430 that are transported from the substrate 400 surface by the vacuum system.

After the monolayer of the boron compound 405 is chemisorbed onto the first refractive metal monolayer 407, excess boron-containing compound is removed from the process chamber by introducing a pulse of a purge gas thereto.

Referring to FIG. 4D, after the process chamber has been purged, a pulse of a second refractory metal compound M₂a₁ is introduced into the process chamber. A layer of the second refractory metal compound is chemisorbed on the boron monolayer 405. The second refractory metal compound typically combines second refractory metal atoms M₂ 440 with one or more reactive species a₁ 425.

The chemisorbed monolayer of the second refractory metal compound reacts with the boron-containing monolayer 405 to form the composite boride layer 409. The reactive species a₁ 425 and b 415 form byproducts a₁b 430 that are transported from the substrate 400 surface by the vacuum system.

After the monolayer of the second refractory metal compound is chemisorbed onto the substrate 400, the excess second refractory metal compound M₂a₁ is removed from the process chamber by introducing another pulse of the purge gas therein.

Thereafter, the boride layer deposition sequence of alternating monolayers of the boron-containing compound and the two refractory metal compounds M₁a₁ and M₂a₁ are repeated until a desired boride layer thickness is achieved.

In FIGS. 4A-4D, boride layer formation is depicted as starting with the chemisorption of the boron-containing monolayer on the substrate followed by monolayers of the two refractory metal compounds. Alternatively, the boride layer formation may start with the chemisorption of monolayers of either of the two refractory metal compounds on the substrate followed by monolayers of the boron-containing compound. Optionally, monolayers of more than two refractory metal compounds may be chemisorbed on the substrate 400.

In a third chemisorption process, the boron-containing monolayers and two or more refractory metal compounds are alternately chemisorbed on the substrate to form a composite boride layer, as illustrated in FIGS. 5A-5D.

FIG. 5A depicts a cross-sectional view of a substrate 500, which may be in a stage of integrated circuit fabrication. A self-limiting monolayer of a first refractory metal compound 507 is chemisorbed on the substrate 500 by introducing a pulse of a first refractory metal compound M₁a₁ into a process chamber similar to that shown in FIG. 1 according to the process conditions described above with reference to FIGS. 2A-2C.

After the monolayer of the first refractory metal compound 507 is chemisorbed onto the substrate 500, excess first refractory metal compound is removed from the process chamber by introducing a pulse of a purge gas thereto.

Referring to FIG. 5B, after the process chamber has been purged, a pulse of a second refractory metal compound M₂a₁ is introduced into the process chamber. A layer of the second refractory metal compound 511 is chemisorbed on the first refractory metal monolayer 507.

After the monolayer of the second refractory metal compound 511 is chemisorbed onto the substrate 500, the excess second refractory metal compound M₂a₁ is removed from the process chamber by introducing another pulse of the purge gas therein.

A pulse of a boron-containing compound 510 is than introduced into the process chamber. A monolayer of the boron-containing compound 505 is chemisorbed on the second refractory metal monolayer 511, as shown in FIG. 5C. The chemisorbed monolayer of the boron-containing compound 505 reacts with the second refractory metal monolayer 511 to form a composite boride layer 509. The reactive species a₁ 525 and b 515 form byproducts a₁b 530 that are transported from the substrate 500 surface by the vacuum system.

After the monolayer of the boron compound 505 is chemisorbed onto the second refractory metal monolayer 511, excess boron-containing compound is removed from the process chamber by introducing a pulse of a purge gas thereto.

Referring to FIG. 5D, after the process chamber has been purged, a pulse of the first refractory metal compound 520 M₁a₁ is introduced into the process chamber. A monolayer of the first refractory metal compound 507 is chemisorbed on the boron monolayer 505.

The chemisorbed monolayer of the first refractory metal compound 507 reacts with the boron-containing monolayer 505 to form the boride monolayer 509. The reactive species a₁ 525 and b 515 form byproducts a₁b 530 that are transported from the substrate 500 surface by the vacuum system.

After the monolayer of the first refractory metal compound 507 is chemisorbed onto the substrate 500, the excess first refractory metal compound M₁a₁ is removed from the process chamber by introducing another pulse of the purge gas therein.

Thereafter, the boride layer deposition sequence of alternating monolayers of the boron-containing compound and the two refractory metal compounds M₁a₁ (520) and M₂a₁ (540) are repeated until a desired boride layer thickness is achieved.

In FIGS. 5A-5D, boride layer formation is depicted as starting with the chemisorption of the first refractory metal monolayer on the substrate followed by monolayers of the second refractory metal compound and the boron-containing compound. Alternatively, the boride layer formation may start with the chemisorption of the monolayer of the boron-containing compound on the substrate followed by the monolayers of the two refractory metal compounds. Optionally, monolayers of more than two refractory metal compounds may be chemisorbed on the substrate 500.

The sequential deposition processes described above advantageously provide good step coverage for the boride layer, due to the monolayer chemisorption mechanism used for forming the boride layer. In particular, boride layer formation using the monolayer chemisorption mechanism is believed to contribute to a near perfect step coverage over complex substrate topographies.

Furthermore, in chemisorption processes, since only one monolayer may be absorbed on the topographic surface, the size of the deposition area is largely independent of the amount of precursor gas remaining in the reaction chamber once a monolayer has been formed.

Referring to FIG. 2C, after the formation of the boride layer 204, a contact layer 206 may be formed thereon to complete the interconnect structure. The contact layer 206 is preferably selected from the group of aluminum, copper, tungsten, and combinations thereof.

The contact layer 206 may be formed, for example, using chemical vapor deposition (CVD), physical vapor deposition (PVD), or a combination of both CVD and PVD. For example, an aluminum layer may be deposited from a reaction of a gas mixture containing dimethyl aluminum hydride (DMAH) and hydrogen (H₂) or argon or other DMAH containing compounds, a CVD copper layer may be deposited from a gas mixture containing Cu⁺²(hfac)₂ (copper hexafluoro acetylacetonate), Cu⁺²(fod)₂ (copper heptafluoro dimethyl octanediene), Cu⁺¹(hfac)TMVS (copper hexafluoro acetylacetonate trimethylvinylsilane), or combinations thereof, and a CVD tungsten layer may be deposited from a gas mixture containing tungsten hexafluoride. A PVD layer is deposited from a copper target, an aluminum target, or a tungsten target.

FIGS. 6A-6C illustrate an alternate embodiment of boride layer formation for integrated circuit fabrication of the interconnect structure. In general, the substrate 600 refers to any workpiece upon which film processing is performed, and a substrate structure 650 is used to generally denote the substrate 600 as well as other material layers formed on the substrate 600. Depending on the specific stage of processing, the substrate 600 may be a silicon semiconductor wafer, or other material layer, which has been formed on the wafer. FIG. 6A, for example, shows a cross-sectional view of a substrate structure 650, having a material layer 602 thereon. In this particular illustration, the material layer 602 may be an oxide (e.g., silicon dioxide). The material layer 602 has been conventionally formed and patterned to provide a contact hole 602H extending to the top surface 600T of the substrate 600.

FIG. 6B shows two boride layers 604, 606 conformably formed on the substrate structure 650. The boride layers 604, 606 are formed by chemisorbing monolayers of a boron-containing compound and one or more refractory metal compounds on the substrate structure 650 as described above with reference to FIGS. 3a-5d. The two boride layers 604, 606 may each comprise one or more refractory metals. The thicknesses of the two or more boride layers 604, 606 may be variable depending on the specific stage of processing. Each boride layer 604, 606 may, for example, have a thickness in a range of about 200 Å to about 5,000 Å.

Referring to FIG. 6C, after the formation of the boride layers 604, 606, a contact layer 608 may be formed thereon to complete the interconnect structure. The contact layer 608 is preferably selected from the group of aluminum, copper, tungsten, and combinations thereof.

The specific process conditions disclosed in the above discussion are meant for illustrative purposes only. Other combinations of process parameters such as precursor and inert gases, flow ranges, pressure and temperature may also be used in forming the boride layer of the present invention.

Although several preferred embodiments, which incorporate the teachings of the present invention, have been shown and described in detail, those skilled in the art can readily devise many other varied embodiments that still incorporate these teachings. 

1. A method for depositing a boride-containing barrier layer on a substrate, comprising: exposing a substrate sequentially to a boron-containing compound and a metal precursor to form a first boride-containing layer during a first sequential chemisorption process; and exposing the substrate to the boron-containing compound, the metal precursor, and a second precursor to form a second boride-containing layer over the first boride-containing layer during a second sequential chemisorption process.
 2. The method of claim 1, wherein the second sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; exposing the substrate to the metal precursor; exposing the substrate to the boron-containing compound; and exposing the substrate to the second precursor.
 3. The method of claim 1, wherein the second sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; exposing the substrate to the metal precursor; and exposing the substrate to the second precursor.
 4. The method of claim 1, wherein the metal precursor comprises tungsten hexafluoride and the boron-containing compound comprises diborane.
 5. The method of claim 4, wherein the substrate is within a process chamber during the second sequential chemisorption process and the process chamber is purged after each exposure of the substrate to the metal precursor, the boron-containing compound, and the second precursor.
 6. The method of claim 4, wherein the substrate is within a process chamber during the second sequential chemisorption process and the second sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the metal precursor; purging the process chamber; exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the second precursor; and purging the process chamber.
 7. The method of claim 4, wherein the substrate is within a process chamber during the second sequential chemisorption process and the second sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the metal precursor; purging the process chamber; exposing the substrate to the second precursor; and purging the process chamber.
 8. The method of claim 1, wherein the substrate is within a process chamber during the second sequential chemisorption process and the second sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the metal precursor; purging the process chamber; exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the second precursor; and purging the process chamber.
 9. The method of claim 1, wherein a contact layer is deposited over the second boride-containing layer.
 10. The method of claim 9, wherein the contact layer comprises tungsten and the contact layer is deposited by a chemical vapor deposition process.
 11. The method of claim 9, wherein the contact layer comprises copper and the contact layer is deposited by a physical vapor deposition process.
 12. The method of claim 1, wherein the first boride-containing layer or the second boride-containing layer is formed at a temperature of less than about 500° C.
 13. The method of claim 12, wherein the temperature is about 400° C. or less.
 14. The method of claim 13, wherein the temperature is about 300° C. or less.
 15. A method for depositing a boride-containing barrier layer on a substrate, comprising: exposing a substrate to a boron-containing compound, a metal precursor, and a second precursor to form a first boride-containing layer during a first sequential chemisorption process; and exposing the substrate sequentially to the boron-containing compound and the metal precursor to form a second boride-containing layer over the first boride-containing layer during a second sequential chemisorption process.
 16. The method of claim 15, wherein the first sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; exposing the substrate to the metal precursor; exposing the substrate to the boron-containing compound; and exposing the substrate to the second precursor.
 17. The method of claim 15, wherein the first sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; exposing the substrate to the metal precursor; and exposing the substrate to the second precursor.
 18. The method of claim 15, wherein the metal precursor comprises tungsten hexafluoride and the boron-containing compound comprises diborane.
 19. The method of claim 18, wherein the substrate is within a process chamber during the first sequential chemisorption process and the process chamber is purged after each exposure of the substrate to the metal precursor, the boron-containing compound, and the second precursor.
 20. The method of claim 18, wherein the substrate is within a process chamber during the first sequential chemisorption process and the first sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the metal precursor; purging the process chamber; exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the second precursor; and purging the process chamber.
 21. The method of claim 18, wherein the substrate is within a process chamber during the first sequential chemisorption process and the first sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the metal precursor; purging the process chamber; exposing the substrate to the second precursor; and purging the process chamber.
 22. The method of claim 15, wherein the substrate is within a process chamber during the first sequential chemisorption process and the first sequential chemisorption process comprises: exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the metal precursor; purging the process chamber; exposing the substrate to the boron-containing compound; purging the process chamber; exposing the substrate to the second precursor; and purging the process chamber.
 23. The method of claim 15, wherein a contact layer is deposited over the second boride-containing layer.
 24. The method of claim 23, wherein the contact layer comprises tungsten and the contact layer is deposited by a chemical vapor deposition process.
 25. The method of claim 23, wherein the contact layer comprises copper and the contact layer is deposited by a physical vapor deposition process.
 26. The method of claim 15, wherein the first boride-containing layer or the second boride-containing layer is formed at a temperature of less than about 500° C.
 27. The method of claim 26, wherein the temperature is about 400° C. or less.
 28. The method of claim 27, wherein the temperature is about 300° C. or less.
 29. A method for depositing a boride-containing barrier layer on a substrate, comprising: exposing a substrate sequentially to a boron-containing compound and a tungsten precursor to form a first boride layer comprising tungsten and boron during a first sequential chemisorption process; and exposing the substrate to the boron-containing compound, the tungsten precursor, and a second precursor to form a second boride-containing layer over the first boride layer during a second sequential chemisorption process, wherein the second precursor comprises an additional element and the second boride-containing layer comprises tungsten, boron, and the additional element.
 30. The method of claim 29, wherein the boron-containing compound comprises diborane. 